SIC bullet proof plates (Use for car,RV,door,wall and so on) B4,B5,B6,B7

Description

One PC B7 Bullet proof plates Size: 100X100CM thick:2.2cm  USD4880.00 (there is no curve)
Sine we have no partner abroad for the time being so sell bulletproof panels only,Not responsible for installation！！
If you are a professional car modification company, you can contact us！
produce time: usually 15~25 working days
Use for car,Vehicle,truck,Helicopter,house,wall,door and other important Dangerous area
if you are interested in this item please contact us and discuss the details
Usually size 100*100cm,80*80cm,60*60cm.100*50cm,80*40cm,60*30cm
and so on or according to client's drawing
Main
Material
Kevlar made from dupont company of U.S.A
Samples price as following:
B5  9*12'' (22.86*30.48cm)  2.20KGS  USD298.00/PC
B6  9*12'' (22.86*30.48cm)  2.50KGS  USD348.00/PC
B7  9*12'' (22.86*30.48cm)  2.80KGS  USD398.00/PC
life expectancy: 5 years
We can help your company refit different cars
we wish company contact us,Because the installation requires some technical support.
we looking for some agents from U.S.A and EUROPE
If your company is very experienced and professional in this area please contact us.
agent company should be can get high profit,According to local market sales.
Material:
SIC (made in china) + Kevlar (made from dupont of U.S.A) or add bulletproof galss
Standard: B4,B5,B6,B7
EN BR4 / NIJ IIIA
Ballistic material :
100% Kevlar (made from dupont of U.S.A)
Surface treatment: anti UV,waterproof and explosion-proof by special coating.
Weight: 8.5kg per sq meter
EN BR6 / NIJ III(III+)
Ballistic material :SIC Lightweight ceramic +
Kevlar (made from dupont of U.S.A)
Surface treatment: anti UV,waterproof and explosion-proof by special coating.
Weight: 34-37kg per sq meter
EN BR7 / NIJ IV
Ballistic material :SIC Lightweight ceramic +
Kevlar (made from dupont of U.S.A)
Surface treatment: anti UV,waterproof and explosion-proof by special coating.
Weight: 38-43kg per sq meter
SIC bullet proof plates, Stronger than AL2O3 ceramic plates
1.
High strength & hardness, good energy absorption capability after cracks
2.
Low density & Light weight, excellent ballistic property
3.
Endure more high temperature and suit for more applications
The contrast of Armour Ceramic Materials
Performance
S-SIC(WNV2)
99% AL2O3
Density
（
g/m3
）
3.10~3.14
3.80
Flexural Strength(4 point bending)  (mpa)
400
300
Hardness Vickers (kg/mm2)
2600
1500
Youngs Modulus
410
310
Fracture Toughness (mpa.m1/2)
4.0
2.5
Maximum Working Temperature
(
℃
)
1600
1400